Hysol™ EA 9309.3NA Molding Compound Epoxy Adhesive, 1qt System, Pink

1031775-34910 MFG #: 9309.3NA
$176.06 / QT
Quantity Pricing
1 $176.06
24 $171.67 Save 2 %
72 $167.48 Save 5 %
Availability: 91 In Stock
  • Brand Name: Henkel
  • Series: EA 9309.3, EA 9309.3NA
  • Product Type: Epoxy Adhesive
  • Hardness: 80Shore D
  • Material Compatibility: Metal
  • Color: Part A:Pink; Part B:Blue
  • Primary Color: Part A:Pink; Part B:Blue
  • Mix Ratio: 100:22
  • Physical Form: Part A:Liquid/Paste; Part B:Gel
  • Cure Time: 3 to 5days
  • Viscosity Measurement: Part A:1500 to 3800; Part B:0.1 to 0.2Pa/s
  • Chemical Composition: Part A:Epoxy Resin, Modified Epoxy Resin, Modified Epoxy Resin, Glass,Oxide,Chemicals, Treated Fumed Silica, Titanium Dioxide; Part B:3,3'-Oxybis(Ethyleneoxy)Bis(Propylamine), Substituted Piperazine, Diethylenetriamine, Silane Derivative
  • Specific Gravity: Part A:1.54; Part B:1
  • VOCs Content: <10g/L
  • Odor: Part A:Epoxy; Part B:Ammoniacal
  • Peel Strength: 48 T Peel; 94 Belllbf/in
  • Cure Type: Room 77°F
  • Elongation at Break: 10%
  • Gel Time: 35min
  • Maximum Operating Temperature: +180°F
  • Container Capacity: Part A:1 pt; Part B:8 oz
  • Applications: Bonding, Aero Space Industry
  • Availability: In Stock
  • Maximum Storage Temperature: 82

The Loctite 9309.3NA is a Series EA 9309.3 epoxy adhesive with a mix ratio of 100:22.

The Loctite 9309.3NA Features:
  • High Shear Strength
  • High Peel Strength
  • Bondline Thickness Control
  • Good Environmental Resistance
The Loctite 9309.3NA Specifications:
  • Brand: Hysol®
  • Series: EA 9309.3
  • Product Type: Epoxy Adhesive
  • Hardness: 80Shore D
  • Material Compatibility: Metal
  • Color: Part A:Pink Part B:Blue
  • Primary Color: Part A:Pink Part B:Blue
  • Mix Ratio: 100:22
  • Physical Form: Part A:Liquid/Paste Part B:Gel
  • Cure Time: 3 to 5days
  • Viscosity Measurement: Part A:1500 to 3800 Part B:0.1 to 0.2Pa/s
  • Chemical Composition: Part A:Epoxy Resin, Modified Epoxy Resin, Modified Epoxy Resin, Glass,Oxide,Chemicals, Treated Fumed Silica, Titanium Dioxide Part B:3,3'-Oxybis(Ethyleneoxy)Bis(Propylamine), Substituted Piperazine, Diethylenetriamine, Silane Derivative
  • Specific Gravity: Part A:1.54 Part B:1
  • VOCs Content: <10g/L
  • Odor: Part A:Epoxy Part B:Ammoniacal
  • Peel Strength: 48 T Peel 94 Belllbf/in
  • Cure Type: Room 77°F
  • Elongation at Break: 10%
  • Gel Time: 35min
  • Tensile Strength‎: 4670psi
  • Maximum Operating Temperature: +180°F
  • Container Capacity: Part A:1 pt Part B:8 oz
  • Applications: Bonding, Aero Space Industry
Pack: Each