The H.B. Fuller 10016704 is a patented Hot Melt Moisture Cure product . It is a oneone-component polyurethane, 100% solids hot melt adhesive. It has characteristics of a pressure sensitive adhesive, but optimal adhesion is achieved from 10 seconds to 15 minutes after application. This product has aggressive hot tack and cures in the presence of moisture to a tough, elastomeric film. It works well in bonding various plastics, woods, metals, and glass substrates.
H.B. Fuller 10016704 Features:- High green strength allowsimmediate handling processingand testing
- Open time of 15 minutes allowingfor extended assembly time.
- Excellent adhesion to a diverse selection of substratesincluding engineering plastics such as polycarbonate,and metals including stainless steel and aluminum.
- Dispense like a one-part hot melt adhesive, reacts with atmospheric moisture to form a tough, cross-linkedurethane polymer network.
- Appearance: Yellow-light brown
- Brookfield Viscosity: Approx. 10,000 mPa.s at 150°C
- Density g/cm3 (20°C): 1.02
- Film Open Time: Up to 15 minutes
- Coverage: 50-120 g/m2
- Application Temperature: Between 140°C and 160°C depending on the operating conditions.
- Application Methods: Can be run on all standard hot melt
- Shelf Life: 6-12 months
Product Description
The H.B. Fuller 10016704 is a patented Hot Melt Moisture Cure product . It is a oneone-component polyurethane, 100% solids hot melt adhesive. It has characteristics of a pressure sensitive adhesive, but optimal adhesion is achieved from 10 seconds to 15 minutes after application. This product has aggressive hot tack and cures in the presence of moisture to a tough, elastomeric film. It works well in bonding various plastics, woods, metals, and glass substrates.
H.B. Fuller 10016704 Features:- High green strength allowsimmediate handling processingand testing
- Open time of 15 minutes allowingfor extended assembly time.
- Excellent adhesion to a diverse selection of substratesincluding engineering plastics such as polycarbonate,and metals including stainless steel and aluminum.
- Dispense like a one-part hot melt adhesive, reacts with atmospheric moisture to form a tough, cross-linkedurethane polymer network.
- Appearance: Yellow-light brown
- Brookfield Viscosity: Approx. 10,000 mPa.s at 150°C
- Density g/cm3 (20°C): 1.02
- Film Open Time: Up to 15 minutes
- Coverage: 50-120 g/m2
- Application Temperature: Between 140°C and 160°C depending on the operating conditions.
- Application Methods: Can be run on all standard hot melt
- Shelf Life: 6-12 months