Loctite 9309.3NA Part A & B Epoxy Adhesive, 6 oz SemKit, Pink/Blue

1041963-34910 MFG #: 9309.3NA
$42.48 / EA
Quantity Pricing
1 $42.48
50 $41.42 Save 2 %
150 $40.41 Save 5 %
Available to Order - 0 on Hand
  • Brand Name: Henkel, Hysol, Loctite
  • Series: EA 9309.3, EA 9309.3NA
  • Product Type: Epoxy Adhesive
  • Hardness: 80Shore D
  • Material Compatibility: Metal
  • Color: Part A:Pink,Part B:Blue
  • Primary Color: Part A:Pink,Part B:Blue
  • Mix Ratio: 100:22
  • Physical Form: Part A:Liquid/Paste,Part B:Gel
  • Cure Time: 3 to 5days
  • Viscosity Measurement: Part A:1500 to 3800,Part B:0.1 to 0.2Pa/s
  • Chemical Composition: Part A:Epoxy Resin, Modified Epoxy Resin, Modified Epoxy Resin, Glass,Oxide,Chemicals, Treated Fumed Silica, Titanium Dioxide,Part B:3,3'-Oxybis(Ethyleneoxy)Bis(Propylamine), Substituted Piperazine, Diethylenetriamine, Silane Derivative
  • Specific Gravity: Part A:1.54,Part B:1
  • VOCs Content: <10g/L
  • Odor: Part A:Epoxy,Part B:Ammoniacal
  • Peel Strength: 48 T Peel,94 Belllbf/in
  • Cure Type: Room 77°F
  • Elongation at Break: 10%
  • Gel Time: 35min
  • Maximum Operating Temperature: +180°F
  • Container Capacity: 6oz
  • Container Type: Semkit
  • Applications: Bonding, Aero Space Industry
  • Container Size: 6 oz
  • Maximum Storage Temperature: 82

Hysol EA 9309.3NA is a toughened two-part paste adhesive. It contains 5 mil/0.13 mm glass beads forbondline thickness control. Hysol EA 9309.3NA bonds metal skins and honeycomb core to yield toughpermanently flexible joints resistant to humidity, water and most common fluids. Its outstanding feature ishigh shear and peel strength to aluminum.

The Loctite 9309.3NA Features:
  • High Shear Strength
  • High Peel Strength
  • Bondline Thickness Control
  • Good Environmental Resistance
The Loctite 9309.3NA Specifications:
  • Brand: Hysol®
  • Series: EA 9309.3
  • Product Type: Epoxy Adhesive
  • Hardness: 80Shore D
  • Material Compatibility: Metal
  • Color: Part A:Pink Part B:Blue
  • Primary Color: Part A:Pink Part B:Blue
  • Mix Ratio: 100:22
  • Physical Form: Part A:Liquid/Paste Part B:Gel
  • Cure Time: 3 to 5days
  • Viscosity Measurement: Part A:1500 to 3800 Part B:0.1 to 0.2Pa/s
  • Chemical Composition: Part A:Epoxy Resin, Modified Epoxy Resin, Modified Epoxy Resin, Glass,Oxide,Chemicals, Treated Fumed Silica, Titanium Dioxide Part B:3,3'-Oxybis(Ethyleneoxy)Bis(Propylamine), Substituted Piperazine, Diethylenetriamine, Silane Derivative
  • Specific Gravity: Part A:1.54 Part B:1
  • VOCs Content: <10g/L
  • Odor: Part A:Epoxy Part B:Ammoniacal
  • Peel Strength: 48 T Peel 94 Belllbf/in
  • Cure Type: Room 77°F
  • Elongation at Break: 10%
  • Gel Time: 35min
  • Tensile Strength‎: 4670psi
  • Maximum Operating Temperature: +180°F
  • Container Capacity: 6oz
  • Container Type: Semkit
  • Applications: Bonding, Aero Space Industry